T1 - Alloying Germanium Nanowire Anodes Dramatically Outperform Graphite Anodes in Full-Cell Chemistries over a Wide Temperature Range
AU - Collins, Gearoid A.
AU - McNamara, Karrina
AU - Kilian, Seamus
AU - Geaney, Hugh
AU - Ryan, Kevin M.
N1 - Publisher Copyright:
©
PY - 2021/2/22
Y1 - 2021/2/22
N2 - The electrochemical performance of Ge, an alloying anode in the form of directly grown nanowires (NWs), in Li-ion full cells (vs LiCoO2) was analyzed over a wide temperature range (-40 to 40 °C). LiCoO2||Ge cells in a standard electrolyte exhibited specific capacities 30× and 50× those of LiCoO2||C cells at -20 and -40 °C, respectively. We further show that propylene carbonate addition further improved the low-temperature performance of LiCoO2||Ge cells, achieving a specific capacity of 1091 mA h g-1 after 400 cycles when charged/discharged at -20 °C. At 40 °C, an additive mixture of ethyl methyl carbonate and lithium bis(oxalato)borate stabilized the capacity fade from 0.22 to 0.07% cycle-1. Similar electrolyte additives in LiCoO2||C cells did not allow for any gains in performance. Interestingly, the capacity retention of LiCoO2||Ge improved at low temperatures due to delayed amorphization of crystalline NWs, suppressing complete lithiation and high-order Li15Ge4 phase formation. The results show that alloying anodes in suitably configured electrolytes can deliver high performance at the extremes of temperature ranges where electric vehicles operate, conditions that are currently not viable for commercial batteries without energy-inefficient temperature regulation.
AB - The electrochemical performance of Ge, an alloying anode in the form of directly grown nanowires (NWs), in Li-ion full cells (vs LiCoO2) was analyzed over a wide temperature range (-40 to 40 °C). LiCoO2||Ge cells in a standard electrolyte exhibited specific capacities 30× and 50× those of LiCoO2||C cells at -20 and -40 °C, respectively. We further show that propylene carbonate addition further improved the low-temperature performance of LiCoO2||Ge cells, achieving a specific capacity of 1091 mA h g-1 after 400 cycles when charged/discharged at -20 °C. At 40 °C, an additive mixture of ethyl methyl carbonate and lithium bis(oxalato)borate stabilized the capacity fade from 0.22 to 0.07% cycle-1. Similar electrolyte additives in LiCoO2||C cells did not allow for any gains in performance. Interestingly, the capacity retention of LiCoO2||Ge improved at low temperatures due to delayed amorphization of crystalline NWs, suppressing complete lithiation and high-order Li15Ge4 phase formation. The results show that alloying anodes in suitably configured electrolytes can deliver high performance at the extremes of temperature ranges where electric vehicles operate, conditions that are currently not viable for commercial batteries without energy-inefficient temperature regulation.
KW - full cell
KW - germanium nanowire
KW - graphite
KW - lithium-ion battery
KW - temperature-controlled electrochemical amorphization
KW - wide temperature performance
UR - http://www.scopus.com/inward/record.url?scp=85100659744&partnerID=8YFLogxK
U2 - 10.1021/acsaem.0c02928
DO - 10.1021/acsaem.0c02928
M3 - Article
AN - SCOPUS:85100659744
SN - 2574-0962
VL - 4
SP - 1793
EP - 1804
JO - ACS Applied Energy Materials
JF - ACS Applied Energy Materials
IS - 2
ER -