Effect of Sb additions on the creep behaviour of low temperature lead-free Sn–8Zn–3Bi solder alloy

Purpose: This paper aims to investigate the creep behaviour of the recently developed Sn–8Zn–3Bi–xSb (x = 0, 0.5, 1.0 and 1.5) low temperature lead-free solder alloys. Design/methodology/approach: An in-house compressive test rig was developed to perform creep tests under stresses of 20–40 MPa and temperature range 25°C–75 °C. Dorn power law and Garofalo hyperbolic sine law were used to model the secondary creep rate. Findings: High coefficient of determination R² of 0.99 is achieved for both the models. It was found that the activation energy of Sn–8Zn–3Bi solder alloy can be significantly increased with addition of Sb, by 60% to 90 kJ/mol approximately, whereas the secondary creep exponent falls in the range 3–7. Improved creep resistance is attributed to solid solution strengthening introduced by micro-alloying. Creep mechanisms that govern the deformation of these newly developed lead-free solder alloys have also been proposed. Originality/value: The findings are expected to fill the gap of knowledge on creep behaviour of these newly developed solder alloys, which are possible alternatives as lead-free interconnecting material in low temperature electronic assembly.