Investigation of In-service Creep Failures of Aircraft Ti-6Al-4V Bolts

Engineering

• Ti-6al-4v 100%
• Creep 100%
• Failure Analysis 50%
• Low-Temperature 50%
• Fracture Mechanism 50%
• Fracture Morphology 50%
• Energy-Dispersive X-Ray Analysis 50%
• Ductile Fracture 50%
• Visual Inspection 50%
• Tension Load 50%
• Macroscopic Deformation 50%
• Landing Gear 50%
• Temperature Creep 50%
• Scanning Electron Microscope 50%
• Jet Aircraft 50%

Material Science

• Aircraft 100%
• Ti-6Al-4V 100%
• Creep 100%
• Scanning Electron Microscopy 50%
• Corrosion 50%
• Electron Microscopy 50%
• Energy Dispersive X Ray Analysis 50%
• Ductile Fracture 50%
• Landing Gear 50%