Oxidative coupling of methane over K/Ni/Ca oxide and K/Ni/Mg oxide catalysts

The oxidative coupling behaviour of a series of K/Ni/Ca oxide catalysts with low nickel-to-calcium ratios has been examined and the results are compared with those for a magnesium-based catalyst. The effect of gas composition and the stability of ethylene under reaction conditions have also been studied. The catalysts were calcined at 1200°C unless otherwise stated. Potassium was added after the calcination stage. It is found that a high calcination temperature of 1200°C is necessary to give a Ca-based catalyst with high activity and selectivity. The catalysts based on MgO were less selective. Substitution of K for Li in the MgO based catalyst gave a slight improvement in the selectivity. A series of experiments was carried out with the K_0.1Ni_0.012 Ca material with the aim of optimising the yield. It was found that the selectivity could be improved by increasing the concentration of CH₄ or by adding CO₂ to the feed. However the addition of CO₂ decreased the activity of the catalyst. The activity could be increased by increasing the H₂O concentration. An increase of the O₂ concentration in the feed from 10.85 to 13% with 31% of CH₄ and 21% H₂O increased the C₂ yield from 15.1% to 17.8%. In a series of experiments in which different concentrations of C₂H₄ were added to the feed, it was found that the main oxidation product of ethylene was CO₂. The formation of ethane was unaffected by the addition of ethylene. It is therefore proposed that two different sites are required for the oxidation of ethylene and the activation of methane to form ethane.