Surface and machining induced damage characterization of abrasive water jet milled carbon/epoxy composite specimens and their impact on tensile behavior

Akshay Hejjaji, Redouane Zitoune, Laurent Crouzeix, Sabine Le Roux, Francis Collombet

Research output: Contribution to journalArticlepeer-review

Abstract

Controlled depth milling of composites structures by abrasive water jet (AWJ) is a new area of machining being explored and knowledge on this is bare minimum. Hence it is essential to investigate surface quality and damage induced to ascertain their mechanical reliability. Here, the mechanism of material removal is manifested by erosive wear. In this study, carbon fiber reinforced plastic (CFRP) laminates are milled using AWJ process and surfaces generated by varying process parameters are characterized using roughness systems, X-ray tomography and scanning electron microscopy (SEM). SEM images reveal presence of damages in form of craters, ridges, broken fibers and embedded abrasive particles. Crater formation due to erosion phenomenon is affected by jet pressure. It is seen that the crater volume increases by around 500% when pressure varies from 80 MPa to 140 MPa. In the literature reviewed correlation between roughness of the machined surface and the mechanical behavior is ambiguous and remains an open problem. Hence, novel attempt has been made to analyze the influence of damage (crater volume) on tensile strength. Mechanical tests on specimens with varying surface texture and crater sizes reveals that tensile strength of machined specimens is more influenced by crater volume rather than surface roughness.

Original languageEnglish
Pages (from-to)1356-1364
Number of pages9
JournalWear
Volume376-377
DOIs
Publication statusPublished - 2017
Externally publishedYes

Keywords

  • Abrasive water jet milling
  • Damage characterization
  • Machining damage
  • Surface topography
  • Tensile strength