TY - JOUR
T1 - The reversibility of Mode-I and -II interlaminar fracture toughness after hydrothermal aging of Carbon/Benzoxazine composites with a thermoplastic toughening interlayer
AU - Nash, N. H.
AU - Young, T. M.
AU - Stanley, W. F.
N1 - Publisher Copyright:
© 2016 Elsevier Ltd.
PY - 2016/9/15
Y1 - 2016/9/15
N2 - In order to determine the ability to reverse the changes in Mode-I and -II critical strain energy release rate (GIC and GIIC) or interlaminar fracture toughness (ILFT) brought about by water ingress, baseline (B) and toughened (T) carbon laminates with two different Benzoxazine resin systems (BZ9120, BZ9130) manufactured using Vacuum Assisted Resin Transfer Moulding (VARTM) were tested under dry, wet and dried environmental conditions. This study represents a "worst-case scenario" approach, in that samples are soaked in hot water until the maximum moisture content is achieved. It was found that neither the Mode-I or Mode-II ILFT of BZ9120B laminates can be restored fully once the saturation point has been reached. Microscopic images of cross-sections showed that saturation causes irreversible damage in the form of intralaminar matrix cracks. Dried samples exhibited brittle matrix behaviour and low fibre/matrix interfacial strength. Toughened samples outperformed baseline samples as they exhibited partial recovery of ILFT.
AB - In order to determine the ability to reverse the changes in Mode-I and -II critical strain energy release rate (GIC and GIIC) or interlaminar fracture toughness (ILFT) brought about by water ingress, baseline (B) and toughened (T) carbon laminates with two different Benzoxazine resin systems (BZ9120, BZ9130) manufactured using Vacuum Assisted Resin Transfer Moulding (VARTM) were tested under dry, wet and dried environmental conditions. This study represents a "worst-case scenario" approach, in that samples are soaked in hot water until the maximum moisture content is achieved. It was found that neither the Mode-I or Mode-II ILFT of BZ9120B laminates can be restored fully once the saturation point has been reached. Microscopic images of cross-sections showed that saturation causes irreversible damage in the form of intralaminar matrix cracks. Dried samples exhibited brittle matrix behaviour and low fibre/matrix interfacial strength. Toughened samples outperformed baseline samples as they exhibited partial recovery of ILFT.
UR - http://www.scopus.com/inward/record.url?scp=84971422882&partnerID=8YFLogxK
U2 - 10.1016/j.compstruct.2016.05.086
DO - 10.1016/j.compstruct.2016.05.086
M3 - Article
AN - SCOPUS:84971422882
SN - 0263-8223
VL - 152
SP - 558
EP - 567
JO - Composite Structures
JF - Composite Structures
ER -