Thermodynamic analysis of methane dry reforming: Effect of the catalyst particle size on carbon formation

Nicolas Abdel Karim Aramouni, Joseph Zeaiter, Witold Kwapinski, Mohammad N. Ahmad

Research output: Contribution to journalArticlepeer-review

Abstract

The effect of catalyst particle size on thermodynamic equilibrium of methane dry reforming and carbon formation has been studied through the Gibbs free energy minimization method taking into account the deviation of carbon formed from graphite Gibbs energy and its dependence on catalyst particle size. Methane and CO2 conversions are maximized at low pressure and high temperature, and a molar H2/CO ratio of 1 is obtained at 1100–1200 K and 5–10 bar. Carbon formation was found to increase with particle diameter, and carbon presence was noticed at conditions of high pressure/low temperature and high temperature/low pressure. Optimal operating conditions were found to be close to carbon limits, highlighting the need for active metal particle size to be less than 5–6 nm to minimize coking. CO was identified as the precursor for carbon at low temperature, while CH4 was found to be the main precursor at high temperature.

Original languageEnglish
Pages (from-to)614-622
Number of pages9
JournalEnergy Conversion and Management
Volume150
DOIs
Publication statusPublished - 2017

Keywords

  • CO
  • Dry reforming
  • Methane
  • Ni catalyst
  • Syngas

Fingerprint

Dive into the research topics of 'Thermodynamic analysis of methane dry reforming: Effect of the catalyst particle size on carbon formation'. Together they form a unique fingerprint.

Cite this