TY - JOUR
T1 - Use of Eucalyptus benthamii wood in the production of Oriented Strand Boards (OSB)
AU - Gorski, Luciane
AU - Da Cunha, Alexsandro Bayestorff
AU - Rios, Polliana D.Angelo
AU - Trianoski, Rosilani
AU - França, Morgana Cristina
AU - De Almeida, Caio Cesar Faedo
AU - Longo, Bruna Laís
PY - 2015
Y1 - 2015
N2 - Use of Eucalyptus benthamii wood in the production of Oriented Strand Boards (OSB). This research aimed to produce OSB with particles of E. benthamii and mix of Pinus taeda and Pinus elliottii. The experimental plan involved five treatments composed of panels with three layers of particles and nominal density of 0,65 g/cm3. The resin phenol formaldehyde and the wax sizing were applied in the amount of 6[%] and 1[%], respectively. The pressing cycle was 8 minutes, temperature of 180°C and specific pressure of 40 kgf/cm2. The assays were performed according to standard ASTM D1037 (1993) and DIN 52362 (1982) and the results were evaluated by Analysis of Variance and Scott-Knott Test. As result, it was observed that the best compositions are obtained in the treatment composed exclusively of Pinus spp particles and in the treatment with particles of Pinus spp in the core layer and the E. benthamii in the outer layers. It was verified potential of Eucalyptus benthamii for the production of OSB when mixed with particles of P. taeda and P. eliiottii, considering that in pure panels it showed unsatisfactory results.
AB - Use of Eucalyptus benthamii wood in the production of Oriented Strand Boards (OSB). This research aimed to produce OSB with particles of E. benthamii and mix of Pinus taeda and Pinus elliottii. The experimental plan involved five treatments composed of panels with three layers of particles and nominal density of 0,65 g/cm3. The resin phenol formaldehyde and the wax sizing were applied in the amount of 6[%] and 1[%], respectively. The pressing cycle was 8 minutes, temperature of 180°C and specific pressure of 40 kgf/cm2. The assays were performed according to standard ASTM D1037 (1993) and DIN 52362 (1982) and the results were evaluated by Analysis of Variance and Scott-Knott Test. As result, it was observed that the best compositions are obtained in the treatment composed exclusively of Pinus spp particles and in the treatment with particles of Pinus spp in the core layer and the E. benthamii in the outer layers. It was verified potential of Eucalyptus benthamii for the production of OSB when mixed with particles of P. taeda and P. eliiottii, considering that in pure panels it showed unsatisfactory results.
UR - http://www.scopus.com/inward/record.url?scp=84953738635&partnerID=8YFLogxK
U2 - 10.5380/rf.v45i4.36280
DO - 10.5380/rf.v45i4.36280
M3 - Article
AN - SCOPUS:84953738635
SN - 0015-3826
VL - 45
SP - 865
EP - 874
JO - Floresta
JF - Floresta
IS - 4
ER -